EFFECT OF THIXOFORMING ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AL-6%SI-3%CU ALLOY
DOI:
https://doi.org/10.11113/jt.v79.11278Keywords:
Aluminium alloy, cooling slope casting, thixoforming, mechanical properties, fracture behaviorAbstract
Thixoforming is a type of semisolid metal (SSM) processing for forming alloys in the semisolid state to near net-shaped products. In the present study, the effect of a thixoforming process on the microstructure and mechanical properties of Al-6Si-3Cu aluminium alloy was investigated. Melt was poured on a cooling slope at 630oC and the samples were obtained through permanent mold casting. They were thixoformed using a hydraulic press after holding at 571oC for 5min to yield a microstructure predominantly composed of α-Al globules and inter-globular Si particles. As-cast and thixoformed samples were characterized using optical microscopy, scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and X-ray diffraction (XRD) as well as hardness measurements and tensile tests. The results indicate that the mechanical properties of thixoformed alloy have improved as compared to permanent mold cast alloy. The ultimate tensile strength of as-cast sample was 210 ± 3.5 MPa and increased to 241 ±3.1 MPa in the thixoformed sample while the yield strength of as-cast alloy was 140 ±4.5 MPa and increased to 176±3.3 MPa in the thixoformed sample. The thixoformed alloy also showed an improvement in elongation to fracture as it increased from 2% in as-cast sample to 3.2% in thixoformed alloy. The fracture of as-cast sample showed a cleavage fracture, whereas in the thixoformed alloy, a combination of dimple and cleavage was observed.
References
Aziz, A. M, Omar, M. Z., Sajuri, Z. and Salleh, M. S. 2016. Microstructural Morphology of Rheocast A319 Aluminium Alloy. Advances in Mechanical Engineering. 8(5): 1-10.
Salleh, M. S., Omar, M. Z., Syarif, J., Alhawari, K. S. and Mohammed, M. N. 2014. Microstructure and Mechanical Properties of Thixoformed A319 Aluminium Alloy. Materials & Design. 64: 142-152.
Salleh, M. S., Omar, M. Z., Syarif, J. and Mohammed, M. N. 2013. Thermodynamic Modelling for Thixoformability of Al–Si Alloys for Semisolid Processing. Advance Science Letters. 19: 3503-3507.
Omar, M.Z., Atkinson, H. V. and Kapranos, P. 2011. Thixotropy in Semisolid Steel Slurries under Rapid Compression. Metall Mater Trans A. 42: 2807-2819.
Salleh, M. S., Omar, M. Z. and Syarif, J. 2015. The Effects of Mg Addition on The Microstructure and Mechanical Properties of Thixoformed Al–5%Si–Cu Alloys. Journal of Alloys and Compounds. 621: 121-130.
Atkinson, H.V. 2012. Alloys for Semi-solid Processing. Solid State Phenomena. 192-193: 16-27.
Cavaliere, P., Cerri, E. and Leo, P. 2005. Effect of Heat Treatments on Mechanical Properties and Damage Evolution of Thixoformed Aluminium Alloys. Materials Characterization. 55(1): 35-42.
Omar, M. Z., Palmiere, E. J., Howe, A. A., Atkinson, H. V. and Kapranos, P. 2005. Thixoforming of a High Performance HP9/4/30 steel. Materials Science and Engineering A. 395(1-2): 53-61.
Fadavi, B. A. and Tahamtan, S. 2009. Fracture Behavior of Thixoformed A356 Alloy Produced by SIMA Process. Journal of Alloys and Compounds. 481: 220-227.
Aziz, A. M, Omar, M. Z., Sajuri, Z. and Salleh, M. S. 2016. Microstructural Changes of Aluminium Alloy A319 on Cooling Slope Plate. Jurnal Teknologi. 78: 6-9.
Chen, G., Du, Z. and Cheng, Y. 2012. Effect of Mechanical Conditions on the Microstructures and Mechanical Properties of Thixoformed Al–Cu–Si–Mg Alloy. Materials & Design. 35: 774-781.
Salleh, M. S., Omar, M. Z., Syarif, J. and Mohammed, M. N. 2014. Thermodynamic Modelling of Al–Si–Cu Alloys for Semisolid Metal Processing. Sains Malaysiana. 43: 791-798.
Haghdadi, N., Zarei-Hanzaki, A., Heshmati-Manesh, S., Abedi, H. R. and Hassas-Irani, S. B. 2013. The Semisolid Microstructural Evolution of a Severely Deformed A356 Aluminum Alloy. Materials & Design. 49: 878-87.
Birol, Y. 2009. Semi-solid Processing of the Primary Aluminium Die Casting Alloy A365. Journal of Alloys and Compounds. 473: 133-8.
Birol, Y. 2007. A357 Thixoforming Feedstock Produced by Cooling Slope Casting. Journal of Materials Processing Technology. 186: 94-101.
Alhawari, K. S., Omar M. Z., Ghazali M. J., Salleh M. S., and Mohammed M. N. 2015. Evaluation of the Microstructure and Dry Sliding Wear Behaviour of Thixoformed A319 Aluminium Alloy. Materials and Design. 76: 169-180.
Ghanbari M., and Shabestari, S.G. 2010. Effect of Plastic Deformation and Semisolid Forming on Iron–manganese rich Intermetallics in Al–8Si–3Cu–4Fe–2Mn alloy. Journal of Alloys and Compounds. 508: 315.
Shabestari, S. G., and Parshizfard, E. 2011. Effect of Semi-Solid Forming on the Microstructure and Mechanical Properties of the Iron Containing Al–Si Alloys. Journal of Alloys and Compounds. 509: 7973-7978.
Simge, G. I., and Nursen, S. 2014. Effect of Fe-rich Intermetallics on the Microstructure and Mechanical Properties of Thixoformed A380 Aluminum Alloy. Engineering Science and Technology, an International Journal. 17(2): 58-62.
Porter, D. A. and Easterling, K. E. 1981. Phase Transformations in Metals and Alloys. Phase Transformations in Metals and Alloys. 132-136.
Yıldırım, M., and Ozyurek, D. 2013. The Effects of Mg Amount on the Microstructure and Mechanical Properties of Al–Si–Mg alloys. Materials & Design. 51: 767-774.
Gaozhan, Z., Yongjin, L., Changjian, S., Fuyou, F. and Chengzhou, L. 2014. The Development of Spheroidal Grains and Thixoforming of AZ91D Magnesium Alloy Treated by Different Routes. Materials Science. 20(4): 419-423.
Mohammed M. N, Omar, M. Z., Salleh, M. S. Alhawari, K. S. and Kapranos, P. 2013. Semi-solid Metal Processing Techniques for Non-dendritic Feedstock Production. The Scientific World Journal. 2013: 1-16.
Downloads
Published
Issue
Section
License
Copyright of articles that appear in Jurnal Teknologi belongs exclusively to Penerbit Universiti Teknologi Malaysia (Penerbit UTM Press). This copyright covers the rights to reproduce the article, including reprints, electronic reproductions, or any other reproductions of similar nature.