A Review of Ultrasonic Tomography for Monitoring the Corrosion of Steel Pipes
DOI:
https://doi.org/10.11113/jt.v73.4468Keywords:
Steel pipe corrosion, cause and effect of corrosion, ultrasonic tomography monitoringAbstract
Infrastructure development is currently taking place rapidly. Designing a dwelling or premises is currently implemented quickly while controlling construction costs in addition to providing guidance on planned development. The architecture uses steel as a main part of the pile and drainage system is connected from sources to consumer. This study focuses on steel pipes that are exposed to corrosion. This problem is considered serious because steel pipes are used not only for the delivery of water supply but also for the delivery of gas and oil to the oil and gas sector, where the same problem occurs. Impacts of the problem of corrosion of steel pipes contribute to the risk of loss to the owner of the premises or industry. An overview of leakage problems, which cause a reduction in the volume of materials or hazards to the environment and consumers, is given, and the occurrence of corrosion in pipelines is evaluated. Monitoring methods use ultrasonic tomography as a major contribution to the implementation of monitoring and assessing the status of pipe durability and ability. This paper looks at the concept of diverse ultrasonic tomography inventions used to assist the process of monitoring of the level of pipeline capacity that will suffer corrosion.
References
I. A. Alam., M. Sadiq. 1989. Metal Contamination of Drinking Water from Corrosion of Distribution Pipes. Environ. Pollut. 57: 167–178.
J. Liu. 1998. Fullerene Pipes. Science. 280: 1253–1256.
D. MartÃnez., R. Gonzalez., K. Montemayor., A. Juarez-Hernandez., G. Fajardo., M. A. L. Hernandez-Rodriguez. 2009. Amine Type Inhibitor Effect on Corrosion-Erosion Wear in Oil Gas Pipes. Wear. 267: 255–258.
R. Kaji., B. J. Azzopardi. 2010. The Effect of Pipe Diameter on the Structure of Gas/Liquid Flow in Vertical Pipes. Int. J. Multiph. Flow. 36: 303–313.
O. Hunaidi. 2000. Detecting Leaks in Water-Distribution Pipes. Inst. Res. Constr: 1–6.
A. S. Tijsseling. 2007. Water Hammer with Fluid-Structure Interaction in Thick-Walled Pipes. Comput. Struct. 85: 844–851.
M. R. Moore., M. Pryor., B. Fields., C. Lucas., M. Phelan., R. E. Besser. 2006. Introduction of Monochloramine Into a Municipal Water System: Impact on Colonization of Buildings by Legionella Spp. Appl. Environ. Microbiol. 72: 378–383.
R. J. De Dear., G. S. Brager. 2002. Thermal Comfort in Naturally Ventilated Buildings: Revisions to ASHRAE Standard 55. Energy and Buildings. 34: 549–561.
C. Flows., C. B. Techniques. 2000. Corrosion Economics. Corrosion. 18: 4–5.
G. Rannou., D. Thierry., N. Lebozec. 2010. Ultrasonic Monitoring Of Steel Corrosion During Accelerated. Test: 1–14.
S. Bonell., O. Brivois., R. Borghi., N. Benahmed. 2006. On the Modelling Of Piping Erosion. Comptes Rendus–Mec. 334: 555–559.
H. Song., V. Saraswathy. 2007. Corrosion Monitoring of Reinforced Concrete Structures - A Review. Int. J. Electrochem. Sci. 2: 1– 28.
P. R. Roberge. 2006. Corrosion Inspection and Monitoring. 1–383.
K. Chiang., T. Mintz. 2008. Techniques for Corrosion Monitoring. 247–264.
H. H. E. Uhlig. 2008. Corrosion Handbook. Corros. Handb. Online: 414–418.
A. Groysman. 2010. Corrosion for Everybody. 1–368.
R. A. Lane. 2005. Under the Microscope: Understanding, Detecting, and Preventing Microbiologically Influenced Corrosion. Journal of Failure Analysis and Prevention. 10–12.
B. F. M. Pots., E. L. J. a Hendriksen. 2000. Corrosion 2000. Corrosion. Paper No.00031.
C. K. Morley., J. Warren., M. Tingay., P. Boonyasaknanon., A. Julapour. 2014. Reprint of: Comparison of modern fluid Distribution, Pressure and Flow in Sediments Associated with Anticlines Growing in Deepwater (Brunei) and Continental Environments (Iran). Mar. Pet. Geol. 55: 230–249.
G. E. Pizarro., I. T. Vargas., P. A. Pastén., G. R. Calle. 2014. Modeling MIC Copper Release from Drinking Water Pipes. Bioelectrochemistry. 97: 23–33.
R. M. Clark., R. C. Haught. 2005. Characterizing Pipe Wall Demand: Implications for Water Quality Modeling. Journal of Water Resources Planning and Management. 131: 208–217.
C. A. Della Rovere., R. Silva., C. Moretti., S. E. Kuri. 2013. Corrosion Failure Analysis Of Galvanized Steel Pipes In A Water Irrigation System. Eng. Fail. 33: 381–386.
T. Juhna., D. Birzniece., S. Larsson., D. Zulenkovs., A. Sharipo., N. F. Azevedo., F. Ménard-Szczebara., S. Castagnet., C. Féliers., C. W. Keevil. 2007. Detection of Escherichia Coli in Biofilms from Pipe Samples and Coupons in Drinking Water Distribution Networks. Appl. Environ. Microbiol. 73: 7456–7464.
M. Snis., J. Olsson. 2008. Reduce Costs for Storage and Distribution of Desalted Water-Use Duplex Stainless Steel. Desalination. 223: 476–486.
Y. Lee. 2013. An Evaluation of Microbial and Chemical Contamination Sources Related to the Deterioration of Tap Water Quality in the Household Water Supply System. Int. J. Environ. Res. Public Health. 10: 4143–4160.
W. A. S. Kumara., B. M. Halvorsen., M. C. Melaaen. 2010. Particle Image Velocimetry for Characterizing the Flow Structure of Oil-Water Flow in Horizontal and Slightly Inclined Pipes. Chem. Eng. Sci. 65: 4332–4349.
Z. Panossian., N. L. de Almeida., R. M. F. de Sousa., G. de S. Pimenta., L. B. S. Marques. 2012. Corrosion of Carbon Steel Pipes and Tanks by Concentrated Sulfuric Acid: A Review. Corrosion Science. 58: 1–11.
A. Niklasson., L.-G. Johansson., J.-E. Svensson. 2004. Atmospheric Corrosion of Historical Organ Pipes: Influence of Acetic and Formic Acid Vapour and Water Leaching On Lead in Metal. Proceedings of the International Conference on Metals Conservation. Canberra. Australia. 273–280.
A. M. Dietrich., D. Glindemann., F. Pizarro., V. Gidi., M. Olivares., M. Araya., A. Camper., S. Duncan., S. Dwyer., A. J. Whelton., T. Younos., S. Subramanian., G. A. Burlingame., D. Khiari., M. Edwards. 2004. Health and Aesthetic Impacts of Copper Corrosion on Drinking Water. Water Science and Technology. 49: 55–62.
V. S. Sastri., 2014. Underground Pipeline Corrosion. 166–211.
C. Q. Li., M. Mahmoodian. 2013. Risk Based Service Life Prediction Of Underground Cast Iron Pipes Subjected To Corrosion. Reliab. Eng. Syst. Saf. 119: 102–108.
X. Xia., Z. Xie., M. Salemi., L. Chen., Y. Wang. 2003. An Index of Substitution Saturation and Its Application. Mol. Phylogenet. Evol. 26: 1–7.
F. Mirzaei., H. A. Alizadeh., A. Taheri-Gravand. 2011. Study Of Water Quality In Different Stations Of Karkheh River Based On Langelier And Ryzner Indices For Determining Potential Clogging Of Droppers. Res. J. Appl. Sci. Eng. Technol. 3: 61–66.
M. Rafique., N. M. Mirza., S. M. Mirza., 2005. Kinetic Study of Corrosion Product Activity in Primary Coolant Pipes of A Typical PWR under Flow Rate Transients And Linearly Increasing Corrosion Rates. J. Nucl. Mater. 346: 282–292.
C. C. Chien., C. M. Kao., C. W. Chen., C. D. Dong., H. Y. Chien. 2009. Evaluation of Biological Stability and Corrosion Potential In Drinking Water Distribution Systems: A Case Study. Environ. Monit. Assess. 153: 127–138.
T. Chong., W. K. Ng., V. Liew. 2014. Revisiting the Performance of MACD and RSI Oscillators. J. Risk Financ. Manag. 7: 1–12.
R. Leiva-GarcÃa., M. J. Muñoz-Portero., J. GarcÃa-Anton. 2011. Influence of Calcium Hypochlorite on The Corrosion Behaviour Of Metal Components Of Residential Water Pipes. International Conference on Energy Environment Entrepreneurship Innovation ICEEEI11. Lanzarote: 76–81.
R. S. Lloyd., J. L. Oliver., M. G. Hughes., C. A. Williams. 2012. The Effects of 4-Weeks of Plyometric Training on Reactive Strength Index and Leg Stiffness in Male Youths. Journal of Strength and Conditioning Research. 26: 2812–2819.
K. Edalati., N. Rastkhah., A. Kermani., M. Seiedi., A. Movafeghi. 2006. the Use of Radiography for Thickness Measurement and Corrosion Monitoring in Pipes. Int. J. Press. Vessel. Pip. 83: 736–741.
W. Dong., T. Moan., Z. Gao. 2012. Fatigue Reliability Analysis of the Jacket Support Structure for Offshore Wind Turbine Considering the Effect of Corrosion and Inspection. Reliability Engineering & System Safety. 106: 11–27.
H. ITO. 1987. Flow in Curved Pipes. JSME International Journal. 30: 543–552.
V. S. Sastri. 2014. Underground Pipeline Corrosion. 166–211.
L. L. Vasiliev. 2005. Heat Pipes in Modern Heat Exchangers. Applied Thermal Engineering. 25: 1–19.
Y. Kleiner., B. Rajani., D. Krys. 2012. Performance of Ductile Iron Pipes: Characterization of External Corrosion Patterns. Journal of Infrastructure Systems. 61.
F. Honarvar., F. Salehi., V. Safavi., A. Mokhtari., A. N. Sinclair. 2013. Ultrasonic Monitoring of Erosion/Corrosion Thinning Rates in Industrial Piping Systems. Ultrasonics. 53: 1251–1258.
D. Chen., N. Bertollo., A. Lau., N. Taki., T. Nishino., H. Mishima., H. Kawamura., W. R. Walsh. 2011. Osseointegration of Porous Titanium Implants with and Without Electrochemically Deposited DCPD Coating in An Ovine Model. Journal of Orthopaedic Surgery and Research. 6: 56.
C. J. Stagg., H. Johansen-Berg. 2013. Studying the Effects of Transcranial Direct-Current Stimulation in Stroke Recovery Using Magnetic Resonance Imaging. Front. Hum. Neurosci. 7: 857.
J. Zhang., S. Xie., X. Wang., Y. Li., Z. Chen. 2012. Quantitative Non-Destructive Testing of Metallic Foam Based on Direct Current Potential Drop Method. IEEE Transactions on Magnetics. 48: 375–378.
K. H. Ryu., I. S. Hwang., N. Y. Lee., Y. J. Oh., J. H. Kim., J. H. Park., C. H. Sohn. 2008. Screening Method For Piping Wall Loss By Flow Accelerated Corrosion. Nucl. Eng. Des. 238: 3263–3268.
M. Nayyar, R. King, and S. Crocker. 2000. Piping Handbook. 1–36.
J. L. Rose., D. Jiao., J. Spanner. 1996. Ultrasonic Guided Wave NDE for Piping. Mater. Eval. 54: 1310–1313.
B. W. Drinkwater., P. D. Wilcox. Ultrasonic Arrays for Non-Destructive Evaluation: A Review. NDT and E International. 39: 525–541.
C. C. Ferraro., A. J. Boyd., G. R. Consolazio. 2013. Evaluation of Damage to Bridge Piers Using Pulse Velocity Tomography. Constr. Build. Mater. 38: 1303–1309.
K. R. Lohr., J. L. Rose. 2003. Ultrasonic Guided Wave and Acoustic Impact Methods for Pipe Fouling Detection. J. Food Eng. 56: 315–324.
M. S. P. Sarah., M. Z. Musa., M. N. Asiah., M. Rusop. 2010. Electrical Conductivity Characteristics of Tio2 Thin Film. Electron. Devices, Syst. Appl. (ICEDSA). Intl Conf 2010.
T. S. Mentzel., K. MacLean., and M. A. Kastner. 2011. Contact-Independent Measurement of Electrical Conductance of A Thin Film with A Nanoscale Sensor. Nano Lett. 11: 4102–4106.
D. Boudinet., M. Benwadih., S. Altazin., R. Gwoziecki., J. M. Verilhac., R. Coppard., G. Le Blevennec., I. Chartier., G. Horowitz. 2010. Influence of the Semi-Conductor Layer Thickness on Electrical Performance of Staggered N- and P-Channel Organic Thin-Film Transistors. Org. Electron. Physics, Mater. Appl. 11: 291–298.
M. Marinkovic., D. Belaineh., V. Wagner., D. Knipp. 2012. On the Origin of Contact Resistances of Organic Thin Film Transistors. Adv. Mater. 24: 4005–4009.
S. Li., Y. G. Kim., S. Jung., H. S. Song., S. M. Lee. 2007. Application of Steel Thin Film Electrical Resistance Sensor for In Situ Corrosion Monitoring. Sensors Actuators, B Chem. 120: 368–377.
K. Datta. D. R. Fraser. 2009. A Corrosion Risk Assessment Model for Underground Piping. Proceedings-Annual Reliability and Maintainability Symposium: 263–267.
J. Cai., S. Osher. 2010. Fast Singular Value Thresholding without Singular Value Decomposition. UCLA CAM Rep. 1–14.
C. Liu., J. B. Harley., Y. Ying., M. H. Altschul., M. Bergés., J. H. Garrett., Jr., D. W. Greve., J. M. F. Moura., I. J. Oppenheim., L. Soibelman. 2013. Ultrasonic Monitoring of a Pressurized Pipe in Operation. Proc. of the Structures Congress. 1903–1913.
M. Baumann., U. Helmke. 2003. Singular Value Decomposition of Time-Varying Matrices. Futur. Gener. Comput. Syst. 19: 353–361.
L. De Chiffre., S. Carmignato., J.-P. Kruth., R. Schmitt., A. Weckenmann. 2014. Industrial Applications of Computed Tomography. CIRP Ann.-Manuf. Technol. 63: 655–677.
H. P. Hong. 1999. Inspection and Maintenance Planning Of Pipeline under External Corrosion Considering Generation of New Defects. Struct. Saf. 21: 203–222.
W. J. S. Gomes., A. T. Beck., T. Haukaas. 2013. Optimal Inspection Planning For Onshore Pipelines Subject To External Corrosion. Reliab. Eng. Syst. Saf. 118: 18–27.
M. J. Bergander. 2003. EMAT Thickness Measurement for Tubes in Coal-Fired Boilers. Appl. Energy. 74: 349–444.
M. P. D Cunha., J. W. Jordan 2005. Improved Longitudinal EMAT Transducer For Elastic Constant Extraction. Proceedings of the IEEE International Frequency Control Symposium and Exposition. 426–432.
W. J. S. Gomes., A. T. Beck. 2014. Optimal Inspection and Design of Onshore Pipelines under External Corrosion Process. Struct. Saf. 47: 48–58.
N. Laycock., P. Laycock., P. Scarf., D. Krouse. 2010. Applications of Statistical Analysis Techniques in Corrosion Experimentation, Testing, Inspection and Monitoring. Shreir’s Corrosion: 1547–1580.
S. Shrestha., J. Simek., A. Smith. 2012. In-Line Inspection EMAT Utilizing an Oblique Field. Corrosion 2012 Conference & Expo. 9.
V. V. Nebrat., E. V. Rabinovich., 2002. Cure Aspects Of Electronic Device ‘EMAT-Express 01’ Applying For The Research Of The Oriental Medicine PSC Phenomenon. Proceedings, 6th Int. Conf. Actual Probl. Electron. Instrum. Eng.
F. Li., D. Xiang., Y. Qin., R. B. Pond., K. Slusarski. 2011. Measurements of Degree of Sensitization (Dos) In Aluminum Alloys Using EMAT Ultrasound. Ultrasonics. 51: 561–570.
S. Dixon., S. E. Burrows., B. Dutton., Y. Fan. 2011. Detection Of Cracks In Metal Sheets Using Pulsed Laser Generated Ultrasound And EMAT Detection. Ultrasonics 51: 7–16.
M. Khalifa., F. Khan., M. Haddara. 2013. Inspection Sampling Of Pitting Corrosion. Insight Non-Destructive Test. Cond. Monit. 55: 290–296.
T. Schwarz., G. P. Pierre., J. Dual. 2013. Rotation of Non-Spherical Micro-Particles by Amplitude Modulation of Superimposed Orthogonal Ultrasonic Modes. J. Acoust. Soc. Am. 133: 1260–8.
B. Li., J. Shi., G. Li., H. Li. 2012. Design of Electromagnetic Pre-Pressure Device for 3-DOF Spherical Ultrasonic Motor. Procedia Engineering. 29: 2393–2398.
M. Hoshina., T. Mashimo., S. Toyama. 2009. Development of Spherical Ultrasonic Motor as a Camera Actuator for Pipe Inspection Robot. IEEE/RSJ International Conference on Intelligent Robots and Systems. IROS 2009: 2379–2384.
J. Yuan., D. W. Wang., H. B. Lin., Q. L. Zhao., D. Q. Zhang., M. S. Cao. 2010. Effect of Zno Whisker Content on Sinterability and Fracture Behaviour of PZT Peizoelectric Composites. J. Alloys Compd. 504: 123–128.
T. Fett., A. Glazounov., M. J. Hoffmann., D. Munz., G. Thun. 2001. On The Interpretation of Different R-Curves For Soft PZT. Eng. Fract. Mech. 68: 1207–1218.
S. Chandrasekaran., K. Lindner. 2000. Power Flow through Controlled Peizoelectric Actuators. J. Intell. Mater. Syst. Struct. 11.
C. Liu, J. B. Harley., N. O’Donoughue., Y. Ying., M. H. Altschul., J. H. Garrett., Jr., J. M. F. Moura., I. J. Oppenheim., L. Soibelman. 2012. Ultrasonic Monitoring of a Pipe Under Operating Conditions. Proc. of SPIE Conference on Smart Structures Technologies for Civil, Mechanical, and Aerospace Systems. 8345: 83450B–83450B.
K. K. Ray., K. Dutta., S. Sivaprasad., and S. Tarafder. 2010. Fatigue Damage of AISI 304 LN Stainless Steel: Role of Mean Stress. Procedia Engineering. 2: 1805–1813.
S. Dutta., A. Das., K. Barat., and H. Roy. 2012. Automatic Characterization of Fracture Surfaces of AISI 304LN Stainless Steel Using Image Texture Analysis. Measurement. 45: 1140–1150.
C. K. Mukhopadhyay., T. Jayakumar., T. K. Haneef., S. Suresh Kumar., B. P. C. Rao., S. Goyal., S. K. Gupta., V. Bhasin., S. Vishnuvardhan., G. Raghava., P. Gandhi. 2014. Use of Acoustic Emission And Ultrasonic Techniques for Monitoring Crack Initiation/Growth During Ratcheting Studies on 304LN Stainless Steel Straight Pipe. Int. J. Press. Vessel. Pip. 116: 27–36.
K. Barat., H. N. Bar., D. Mandal., H. Roy., S. Sivaprasad., S. Tarafder. 2014. Low Temperature Tensile Deformation and Acoustic Emission Signal Characteristics Of AISI 304LN Stainless Steel. Mater. Sci. Eng. A. 597: 37–45.
Lenntech Com. 2012. Stainless Steel Mechanical Properties. Stainless steel mechanical properties, 2012. [Online].Available:http://www.ezlok.com/TechnicalInfo/MPStainlessSteel.html.
A. Hajnorouzi., R. Afzalzadeh., and F. Ghanati., 2014. Ultrasonic Irradiation Effects On Electrochemical Synthesis Of Zno Nanostructures. Ultrason. Sonochem. 21: 1435–1440.
A. Emadi., H. Wu., G. De Graaf., K. Hedsten., P. Enoksson., J. H. Correia., R. F. Wolffenbuttel. 2010. An UV Linear Variable Optical Filter-Based Micro-Spectrometer. Procedia Engineering. 5: 416–419.
P. M. Donaldson., H. Strzalka., P. Hamm. 2012. High Sensitivity Transient Infrared Spectroscopy: A UV/Visible Transient Grating Spectrometer with a Heterodyne Detected Infrared Probe. Optics Express. 20: 12761.
G. Rinke., C. Hartig. 1994. Multicomponent Process UV Spectrometer. Tech. Mess. 61: 204–207.
J. A. G. Juárez., G. Rodriguez., V. Acosta., E. Riera. 2010. Power Ultrasonic Transducers with Extensive Radiators for Industrial Processing. Ultrason. Sonochem. 17: 953–964.
T. Bagci., A. Simonsen., S. Schmid., L. G. Villanueva., E. Zeuthen., J. Appel., J. M. Taylor. 2014. Optical Detection of Radio Waves Through a Nanomechanical Transducer. Nature. 507 81–5.
C. R. Bowen., L. R. Bradley., D. P. Almond., P. D. Wilcox. 2008. Flexible Piezoelectric Transducer for Ultrasonic Inspection Of Non-Planar Components. Ultrasonics. 48: 367–375.
Downloads
Published
Issue
Section
License
Copyright of articles that appear in Jurnal Teknologi belongs exclusively to Penerbit Universiti Teknologi Malaysia (Penerbit UTM Press). This copyright covers the rights to reproduce the article, including reprints, electronic reproductions, or any other reproductions of similar nature.