EFFECT OF LOADING RATE ON FRACTURE BEHAVIOUR OF Mg-Al-Zn ALLOYS

Authors

  • Noradila Abdul Latif Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor, Malaysia
  • Zainuddin Sajuri Department of Mechanical and Materials Engineering, Faculty of Engineering and Built Environment, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor, Malaysia
  • Junaidi Syarif Mechanical Engineering Department, College of Engineering, University of Sharjah, PO Box:27272, Sharjah, UAE
  • Yukio Miyashita Department of Mechanical Engineering, Nagaoka University of Technology, 1603-1, Kamitomioka, Nagaoka, Niigata 940-2188, Japan

DOI:

https://doi.org/10.11113/jt.v78.9151

Keywords:

oading rate, three-point bending, ductile, elastic-plastic fracture, Mg-Al-Zn alloys.

Abstract

In recent years, magnesium alloys are widely used for automotive applications as structural components due to its lightweight property and high specific strength. In this regards, magnesium alloys are subjected to high velocity and impact loads during accident. Hence, understanding the impact and dynamic behaviours of magnesium alloys are essential. In this study, the effect of loading rates on the fracture behaviour of Mg-Al-Zn alloys was investigated using pre-cracked single-edge notched bending (SENB) specimens. Three-point bending tests were conducted at different loading rates of 5, 50 and 500 mm/min. The Mg-Al-Zn alloys that used in the present study were extruded AZ31 and AZ61 magnesium alloys. From the load-load line displacement results, both alloys exhibited nonlinear fracture behaviour. The maximum load (Pmax) of these two alloys increased with increasing loading rate. Comparing both alloys, AZ61 exhibited higher Pmax than that of AZ31 due to the higher volume of b-phase and smaller grain size in AZ61. Fracture surface observation revealed that both alloys fractured in ductile manner with large scale yielding and high shear lips ratio at all loading rates.

References

Gupta, M., and Sharon, N. M. L. 2011. Magnesium, Magnesium Alloys, and Magnesium Composites, John Wiley & Sons Inc.

Kainer, K. U. 2004. The Current State of Technology and Potential for Further Development of Magnesium Applications, in: K. U. Kainer, Magnesium-Alloys and Technology, WILEY-VCH. 1-22.

Dargusch, M. S., Pettersen, K., Nogita, K.,Nave, M. D. and Dunlop, G. L. 2006. The Effect of Aluminium Content on the Mechanical Properties and Microstructure of Die Cast Binary Magnesium-Aluminium Alloys. Materials Transactions. 47(4): 977-982.

Sillekens, W. H., and Bormann, D. 2012. Biomedical Applications of Magnesium Alloys, in: C. Bettles, M. Barnett, Advances In Wrought Magnesium Alloys: Fundamentals Of Processing. Properties And Applications. Woodhead Publishing Limited. 427-454.

Sajuri, Z. 2010. Effect of Manufacturing Processes on Fatigue Strength of Magnesium Alloys. Advances in Materials Processing. 2: 305-334.

Chamos, A. N., Pantelakis, S. G., Haidemenopoulos, G. N. and Kamoutsi, E. 2008. Tensile and Fatigue Behaviour of Wrought Magnesium Alloys AZ31 and AZ61. Fatigue and Fracture of Engineering Materials and Structures. 31(9): 812-821.

Barnett, M. R. 2007. Twinning and the Ductility of Magnesium Alloys. Part I. "Tension" twins, Materials Science and Engineering A. 464: 1-7.

ASTM E399. 2008. Standard Test Method for Linear Elastic Plane Strain Fracture Toughness KIC of Metallic Materials.

Joyce, J. A. 1989. Recent Developments in Drop Tower J Integral Testing Of Elastic Plastic Structural Steels. International Conference on Fracture. 7: 197-204.

Li, B., Joshi, S., Azevedo, K., Ma, E., Ramesh, K. T., Figueiredo, R. B. and Langdon,T. G. 2009. Dynamic Testing at High Strain Rates of an Ultrafine-grained Magnesium Alloy Processed by ECAP, Materials Science and Engineering A. 517: 24-29.

Feng, F., Huang, S., Meng, Z., Hu, J., Lei, Y., Zhou, M., Wu, D. and Yang, Z. 2014. Experimental Study on Tensile Property of AZ31B Magnesium Alloy at Different High Strain Rates and Temperatures. Materials and Design. 57: 10-20.

Li, Y. and Enoki, M. 2007. Evaluation of the Twinning Behavior of Polycrystalline Magnesium at Room Temperature by Acoustic Emission. Materials Transactions 48(6): 1215-1220.

Li, Y. and Enoki, M. 2007. Evaluation of the Twinning Behavior of Polycrystalline Magnesium at Room Temperature by Acoustic Emission. Materials Transactions. 48(6): 1215-1220.

Rolfe, S. T. and Barsom, J. M. 1977. Fracture and Fatigue Control in Structures: Applications of Fracture Mechanics. ASTM International.

Vander Voort, G. F. 1978. Macroscopic Examination Procedures for Failure Analysis. J. L. McCall, P. M. Frence, Metallography in Failure Analysis, Springer US, 33-63.

Downloads

Published

2016-06-21

Issue

Vol. 78 No. 6-9: Advances in Research on Automotive Technology Vol. 1

Section

Science and Engineering

License

Copyright of articles that appear in Jurnal Teknologi belongs exclusively to Penerbit Universiti Teknologi Malaysia (Penerbit UTM Press). This copyright covers the rights to reproduce the article, including reprints, electronic reproductions, or any other reproductions of similar nature.

How to Cite

EFFECT OF LOADING RATE ON FRACTURE BEHAVIOUR OF Mg-Al-Zn ALLOYS. (2016). Jurnal Teknologi (Sciences & Engineering), 78(6-9). https://doi.org/10.11113/jt.v78.9151