IMPORTANCE OF FLOW VALUES IN QUALITATIVE EVALUATION OF CARBON NANOTUBE REINFORCED CEMENTITIOUS MATRIX
DOI:
https://doi.org/10.11113/mjce.v25.15843Keywords:
Carbon nanotubes, surface treated, dispersion, compressive strength, flow valuesAbstract
In the field of nanotechnology, Carbon nanotube (CNT) has the prime focus as one of the most important areas of research. A major difficulty of producing CNT-cement composites is the attainment of uniform dispersion of CNT. CNT has a tendency to agglomerate creating zones of weakness in composite materials. In this study, a parametric study was carried on surface treated multiwalled carbon nanotubes (MWNT) reinforced cementitious composites having different mix proportions and an attempt was made to establish a relation between compressive strengths and flow values of composites samples. It was observed that the effect of flow values on compressive strength was most pronounced at 28 day. Composites made with surfactant exhibited less fluctuation in flow values and corresponding compressive strengths. A higher flow value of MWNT added composites, having same mix proportion, represents more uniform distribution of MWNT within the cement grains and more stable mix. Furthermore, less variation in flow values represents more stable dispersion technique to distribute CNT within cement matrix.References
American Society for Standard Testing and Materials (ASTM). (2008) Standard Test Method for Compressive Strength of Hydraulic-Cement Mortars. ASTM C 109-07, West Conshohocken, PA.
American Society for Standard Testing and Materials (ASTM). (2008) Standard Test Method for Flow of Hydraulic Cement Mortar. ASTM C 1437-07, West Conshohocken, PA.
Coleman, J. N., Khan, U. Blau, W. Z., and Gun'ko, Y. K. (2006) Small but strong: A review of the mechanical properties of carbon nanotube-polymer composites. Carbon, 44 (9) 1624- 1652.
Gay, C., and Sanchez, F. (2010) Performance of Carbon Nanofiber-Cement Composites with a High-Range Water Reducer. Journal of the Trans-portation Research Board, No. 2142,
-113.
Konsta-Gdoutos, M. S., Metaxa, Z. S., and Shah, S. P. (2010) Highly Dis-persed Carbon Nanotube Reinforced Cement Based Materials. Cement and Concrete Research, 40, 1052-1059.
Li, H., Xiao, H. G., Yuan, J., and Ou, J. (2004) Microstructure of Cement Mortar with Nanoparticles.
Composites: Part B (35), 185-189.
Marrs, B., Andrews, R., and Pienkowski, D. (2007) Multiwall Carbon Nano tubes Enhance the Fatigue Performance of Physiologically Maintained Methyl Methacrylate-Styrene
Copolymer. Carbon, 45 (10) 2098-2104.
Manzur, T., and Yazdani, N. (2010) Strength Enhancement of Cement Mor-tar with Carbon
Nanotubes: Early Results and Potential. Journal of the Transportation Research Board. No. 2142, 102-108.
Yazdanbakhsh, A., Grasley, Z., Tyson, B., and Abu Al-Rub, R. K. (2010) Distribution of Carbon Nanofibers and Nanotubes in Cementitious Composites. Journal of the Transportation Research Board, No. 2142, 89-95.